Low Alloyed Tool Steel plate DIN 90MnCrV8
Delivery term:The date of payment from buyers deliver within days-
Price:
Negotiable
- minimum:
- Total supply:
-
Delivery term:
The date of payment from buyers deliver within days
-
seat:
Beijing
-
Validity to:
Long-term effective
-
Last update:
2017-09-08 23:41
-
Browse the number:
133
+
Shanghai Bozhong Metal Group Co. Ltd
- Contactaixin:
Contactaixin:
bozhong(Ms.)
-
telephone:
-
Area:
Beijing
Address:BUILDING 32#, NO. 518, XINZHUAN ROAD, SONGJIANG, Shanghai, Shanghai, China (201612)
- Website:
+
Model Number: ZXL151
Brand Name: Baosteel, TISCO
Key Specifications/Special Features:
DescriptionCold work tool steel with high dimensional stability at heat treatment. Very high resistance to cracking. High mach inability, medium toughness and resistance to wear.ApplicationsMeasuring tools, machine knives for the wood, paper and metal industry, cold cutting shear blades, thread cutting tools.Chemical Composition (in weight %)C 0.90
Si 0.25
Mn 2.00
Cr 0.35
V 0.13
Physical properties (average values) at ambient temperature
Modulus of elasticity [103xN/mm2]: 210
Density [g/cm3]: 7.85
Thermal conductivity [W/m. K]: 30.0
Electric resistivity [Ohm mm2/m]: 0.35
Specific heat capacity [J/g. K]: 0.46
Soft annealing
Heat to 690-720℃, cool slowly in furnace. This will produce a maximum Brinell hardness of 229.
Stress relieving
Stress relieving to remove machining stresses should be carried out by heating to 650℃, holding for 1 hour at heat, followed by air cooling. This operation is performed to reduce distortion during heat treatment.
Hardening
Harden from a temperature of 790-820℃followed by oil or warm bath (180-220℃) quenching. Hardness after quenching is 63-65 HRC.
Forging
Hot forming temperature: 1050-850℃.
Corrosion resistance
Corrosion resistance of this alloy is better than that of plain carbon steels. However it will rust unless given protective treatment.
Specifications:
Grade: DIN 90MnCrV8
Standards: DIN, GB, AISI
Length: 1500-6000mm
Width: 100-1250mm
Thickness: 0.3-200mm
Certification: ISO
Technical treatment: cold-rolled and hot rolled
Packing and delivery
Packing: standard export seaworthy package or as customers’requirements.
Delivery: 7-20 days after received deposit of T/T.
Si 0.25
Mn 2.00
Cr 0.35
V 0.13
Physical properties (average values) at ambient temperature
Modulus of elasticity [103xN/mm2]: 210
Density [g/cm3]: 7.85
Thermal conductivity [W/m. K]: 30.0
Electric resistivity [Ohm mm2/m]: 0.35
Specific heat capacity [J/g. K]: 0.46
Soft annealing
Heat to 690-720℃, cool slowly in furnace. This will produce a maximum Brinell hardness of 229.
Stress relieving
Stress relieving to remove machining stresses should be carried out by heating to 650℃, holding for 1 hour at heat, followed by air cooling. This operation is performed to reduce distortion during heat treatment.
Hardening
Harden from a temperature of 790-820℃followed by oil or warm bath (180-220℃) quenching. Hardness after quenching is 63-65 HRC.
Forging
Hot forming temperature: 1050-850℃.
Corrosion resistance
Corrosion resistance of this alloy is better than that of plain carbon steels. However it will rust unless given protective treatment.
Specifications:
Grade: DIN 90MnCrV8
Standards: DIN, GB, AISI
Length: 1500-6000mm
Width: 100-1250mm
Thickness: 0.3-200mm
Certification: ISO
Technical treatment: cold-rolled and hot rolled
Packing and delivery
Packing: standard export seaworthy package or as customers’requirements.
Delivery: 7-20 days after received deposit of T/T.
Shipping Information:
- FOB Port: Shanghai
- Lead Time: 7 - 15 days
Main Export Markets:
- Asia
- Australasia
- Central/South America
- Eastern Europe
- Mid East/Africa
- North America
- Western Europe